SAE AS 22759-33:2000 pdf download

SAE AS 22759-33:2000 pdf download

Temperature rating: 200°C (392°F) maximum continuous conductor temperature.
Voltage rating: 600 volts (rms) at sea level.
Acid resistance: No requirement.
Blocking: 230°C ±3°C (446°F ± 5.4°F).
Color: In accordance with MIL-STD-1 04, class 1 ; white preferred. Conformity of color to the limits of MIL-STD-1 04 shall not be required after crosslinking proof test or life cycle oven exposure.
Color striping or banding durability: 1 25 cycles (250 strokes) (min), 500 grams weight.
Crosslinking proof test: 7 hours at 300°C ±3°C (572°F ±5.4°F). Quality conformance test, group II. Requirements and procedures as for life cycle except for time and temperature.
Dielectric test after immersion: 2,500 volts (rms), 60 Hz.
Flammability: Quality conformance test, group II. For requirements and procedures see below.
Humidity resistance: After humidity exposure, wire shall meet the requirements for initial insulation resistance.
Identification of product: Not required for size 24 and smaller. Color code designator not required.
Identification durability: 1 25 cycles (250 strokes) (min), 500 grams weight.
Immersion: For procedure see below.
Impulse dielectric test: 8.0 kilovolts (peak), 1 00 percent test.
Insulation resistance, initial: 5,000 megohms for 1 ,000 feet (min).
Insulation thickness: 0.005 inch (min).
Life cycle: 500 hours at 230°C ±3°C (446°F ±5.4°F). Dielectric test, 2,500 volts (rms), 60 Hz. Procedure to use mandrels coated with polytetrafluoroethylene in the form of either enamel or wrapped tape, such that the diameter of the mandrels,after coating, still conform to the requirements of performance details, table II.
Low temperature (cold bend):
Bend temperature, -65°C ±3°C (-85°F ±5.4°F).
Dielectric test, 2,500 volts (rms), 60 Hz.
Physical properties of insulation: Pulled at 2 inches per minute.
Tensile strength, 5,000 lbf/in 2 (min).
Elongation, 75 percent (min).
Propellant resistance: No dielectric breakdown. For procedure see below.
Shrinkage: 0.1 25 inch (max) at 230°C ±3°C (446°F ±5.4°F).
Smoke: 250°C ±5°C (482°F ±9°F); no visible smoke.
Solderability: All conductors shall be tested in accordance with MIL-STD-202, method 208 without steam aging.
Spark test of primary insulation: Not applicable.
Surface resistance: 500 megohms – inches (min), initial and final readings.
Thermal shock resistance:
Oven temperature, 200°C ±3°C (392°F ±5.4°F).
Maximum change in measurement, 0.060 inch.
Wicking: Not applicable.
Wire length requirements: Schedule B.
Wrap test:
Wrap back test.
Oven temperature, 31 3°C ±3°C (595°F ±5.4°F).
Flammability requirements and procedure:
The flammability test of MIL-W-22759 shall be modified for the wire of this specification sheet as follows: The specified test burner shall be used without the wing top flame spreader and shall be adjusted to furnish a 3-inch conical flame with an inner cone approximately 1 inch in height and a temperature of 955°C ±30°C (1 751 °F ±54°F) at its hottest point. A sheet of facial tissue conforming to UU-T-450 shall be suspended taut and horizontal 9-1 /2 inches below the marked point on the wire specimen in the test chamber and at least 1 /2 inch above the floor of the chamber. The period of application of the hot flame tip to the marked point on the wire specimen shall be 30 seconds for all sizes of wire. Observations shall include time of burning after removal of the test flame, final distance of flame travel on the wire above the test mark, and presence or absence of flame in the facial tissue due to incendiary drip from the specimen. Requirements shall be: